| About |
|---|
| SCLAIR® 17A is a High Density Polyethylene material. It is available in North America for coextrusion. Important attributes of SCLAIR® 17A are: Butene Comonomer Food Contact Acceptable Good Processability Processing Aid Typical applications include: Additive/Masterbatch Food Contact Applications&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Grease resistance,Solvent resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.45 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 67 | ASTM D2240 | |
| friction coefficient | |||
| Blown film | 0.24 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 38 | µm | |
| Secant modulus | |||
| 1% secant, TD, 38 µ m, blow molded film | 900 | MPa | ASTM D882 |
| 1% secant, MD, 38 µ m | 630 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture, 38 µ m, blow molded film | 20.0 | MPa | ASTM D882 |
| TD, yield, 38 µ m, blow molded film | 20.0 | MPa | ASTM D882 |
| MD, fracture, 38 µ m, blow molded film | 45.0 | MPa | ASTM D882 |
| MD, yield, 38 µ m, blow molded film | 22.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 38 µ m, blow molded film | 750 | % | ASTM D882 |
| MD, fracture, 38 µ m, blow molded film | 650 | % | ASTM D882 |
| Drop hammer impact | |||
| 38 µ m, blow molded film | 40 | g | ASTM D1709-A |
| tear strength | |||
| MD, 38 µ m, blow molded film | 22 | g | ASTM D1922 |
| Elmandorf tear strength | |||
| TD, 38 µ m, blow molded film | 880 | g | ASTM D1922 |
| Nitrogen transfer rate | |||
| 73 ℃, 38 µ m, blow molded film, 0.0% RH | 1920 | cm³/m²/24 hr | ASTM D1434 |
| Water vapor transmittance | |||
| 38 ℃, 100% RH, 38 µ m, blow molded film | 4.0 | g/m²/24 hr |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Low friction puncture | |||
| Blow molded film, 38.0 µ m | 230 | J/cm | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |