| High impact resistance, non-blooming flame retardant polypropylene compound for UL94-V0 injection molding applications.&& |
| Product Description | |
|---|---|
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Negative |
| Features | High impact resistance,Low to No Fogging,Flame Characteristics,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 to 1.02 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 15 to 21 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| yield | > 25.5 | MPa | ASTM D638 |
| fracture | > 10.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 100 | % | ASTM D638 |
| Bending modulus | > 1380 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | > 64 | J/m | ASTM D256 |
| Drop hammer impact | > 16.3 | J | ASTM D3029 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 | |
| Extreme oxygen index | > 28 | % | ASTM D2863 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |