| UF914 is a melt blend grade for blown film applications. UF914 has good optical properties and good processability.&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Smoothness,Optical performance,High anti-blocking,Inoxidizability |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.1 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| tensile strength | ASTM D882 | ||
| MD, fracture, 40 µ m, blow molded film | 38.7 | MPa | ASTM D882 |
| TD, fracture, 40 µ m, blow molded film | 36.8 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 40 µ m, blow molded film | 700 | % | ASTM D882 |
| TD, fracture, 40 µ m, blow molded film | 720 | % | ASTM D882 |
| Drop hammer impact | |||
| 40 µ m, blow molded film | 120 | g | ASTM D1709 |
| tear strength | ASTM D1922 | ||
| MD，40 µm | 44.1 | kN/m | ASTM D1922 |
| TD，40 µm | 88.3 | kN/m | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 40.0 µ m, blow molded film | 75 | ASTM D2457 | |
| Haze | |||
| 40 µ m, blow molded film | 7.5 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |