| SEPAZ CON E1366 is a CF 30% reinforced PA66 product. SEPAZ CON E1366 has good properties with excellent mechanical properties and 10³ ohm/sq surface electric resistivity.&& |
| Product Description | |
|---|---|
| Supplier | Mando |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.050 | % | ASTM D955 |
| TD | 0.25 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.020 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 255 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| Bending modulus | 17900 | MPa | ASTM D790 |
| bending strength | 343 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 88 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 240 | ℃ | ASTM D648 |
| Melting peak temperature | 260 | ℃ | ASTM D3418 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | < 1.0E+3 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 270 to 290 | °C | |
| Barrel front temperature | 270 to 290 | °C | |
| Nozzle temperature | 280 to 300 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |