| About |
|---|
| Shin-Etsu KE-1950-10 is a liquid injection molding silicone. It is supplied as two components which are mixed in a 1:1 ratio to ensure easy and accurate blending. The viscosity of KE-1950-10 is low enough to allow easy pumping through most injection molding systems. Rapid cure time at elevated temperature. Typical Applications O-rings. – Diaphragms. Capping. Rubber rollers. Connector packings. Other electrical parts&& |
| Product Description | |
|---|---|
| Supplier | Shin-Etsu |
| Generic | 硅橡胶,HTV |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Low Viscosity,Fast Cure |
| Availabilitys | North America |
| Process Methods | Liquid injection molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | 13 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 3.90 | MPa | |
| 100% strain | 0.207 | MPa | |
| Tensile strain | |||
| fracture | 700 | % | |
| tear strength | 9.98 | kN/m | |
| Compression deformation | |||
| 180℃，22 hr | 8.0 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Post curing time | |||
| 200℃ | 4.0 | hr |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Curing time | 0.083 | hr |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |