| About |
|---|
| Shinkolite L is a Polymethyl Methacrylate Acrylic material. It is available in Asia Pacific, Europe, or North America. Primary attribute of Shinkolite L: Low to No Odor/Taste.&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | Low odor |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 , ISO 1183 |
| Water absorption rate | |||
| 24hr | 0.30 | % | ASTM D570 |
| 23℃，24hr | 0.30 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 17 | kJ/m² | ISO 179/1fU |
| Impact strength of cantilever beam notch | 2.00 | kJ/m² | ASTM D256 |
| Impact strength of cantilever beam notch | 2.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 100 | ℃ | ASTM D648，ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ASTM D696，ISO 11359-2 |
| specific heat | 1500 | J/kg/℃ | |
| Thermal conductivity coefficient | 0.21 | W/m/K | ASTM C177 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+16 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 20 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 4.00 | ASTM D150 | |
| 1 kHz | 4.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 0.060 | ASTM D150 | |
| 1 kHz | 0.040 | ASTM D150 | |
| 1 MHz | 0.020 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| — | 33 | mm/min | ISO 1210 |
| — | 33 | mm/min | ASTM D635 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | |||
| — | 1.490 | ASTM D542 | |
| — | 1.490 | ISO 489 | |
| Transmittance | |||
| total | 93.0 | % | ASTM D1003 |
| total | 93.0 | % | ISO 13468-1 |
| Haze | |||
| — | 0.50 | % | ASTM D1003 |
| — | 0.50 | % | ISO 14782 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Loss of soluble substances | |||
| after immersion | 0.0 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 100 | ASTM D785 , ISO 2039-2 | |
| Tensile modulus | 3200 | MPa | ASTM D638 , ISO 527-2/1B/1 |
| tensile strength | |||
| fracture | 75.0 | MPa | ASTM D638 , ISO 527-2/1B/5 |
| Tensile strain | |||
| fracture | 4.5 | % | ASTM D638 , ISO 527-2/1B/5 |
| Bending modulus | 3200 | MPa | ASTM D790 , ISO 178 |
| bending strength | |||
| — | 120 | MPa | ISO 178 |
| fracture | 120 | MPa | ASTM D790 |
| Compression modulus | 3200 | MPa | ASTM D695 , ISO 604 |
| compressive strength | 120 | MPa | ASTM D695，ISO 604 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 28°C, 75%RH |
| 3. Method A (Short-Time) |
| 4. Method A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |