| About |
|---|
| Silopren RTV 2 K Gel TP 3607 is a solvent free, low viscosity, two component silicone rubber which crosslinks into a gel-like product by an addition reaction at room temperature. The two components A and B are mixed in a ratio of 1:1. The gel-like vulcanizate is transparent, dimensionally stable and has a high elongation at break. Key Features and Benefits solvent-free, low viscosity, room-temperature vulcanizing transparent and dimensionally stable&& |
| Product Description | |
|---|---|
| Supplier | Momentive |
| Generic | 硅橡胶,RTV-2 |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Low Viscosity,Good Tensile Strength,Room temperature cure |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shaw’s A | 17 | DIN 53505 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 1.0 | ||
| Component B | 按重量计算的混合比: 1.0 | ||
| Storage period | |||
| 20℃ | 26 | wk |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| colour | |||
| — | Clear/Transparent | ||
| — | Clear/Transparent | ||
| Density | |||
| — | 0.980 | g/cm³ | |
| — | 0.980 | g/cm³ | |
| viscosity | |||
| — | 5.0 | Pa·s | |
| — | 5.0 | Pa·s | |
| storage stability | |||
| 23℃ | 15 | min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Part B |
| 3. Part A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |