Silopren® LSR 2540

About
Silopren LSR 2540 is a two-component liquid silicone rubber especially developed for the coating of textiles and glassfibre fabrics. Key Features and Benefits Vulcanisates consisting of Silopren LSR 2540 are distinguished by the following properties: low viscosity excellent thermal stability high stability and flexibility at low temperatures good rubber-like properties long service life at dynamic stress high stability to ozone and ultraviolet light outstanding resistance to ageing excellent dielectric behaviour over a wide range of temperatures not readily combustible, does not melt or drip easy pigmentable with the LSR Colour Pastes Potential Applications Because of the outstanding properties Silopren LSR 2540 is particularly suitable for the following applications: textile coating for protective suits or conveyor belts, coating of glasfibre fabric sleeves, coating of fabrics for compensators, tents and other technical applications s.o.&&

About

Silopren LSR 2540 is a two-component liquid silicone rubber especially developed for the coating of textiles and glassfibre fabrics. Key Features and Benefits Vulcanisates consisting of Silopren LSR 2540 are distinguished by the following properties: low viscosity excellent thermal stability high stability and flexibility at low temperatures good rubber-like properties long service life at dynamic stress high stability to ozone and ultraviolet light outstanding resistance to ageing excellent dielectric behaviour over a wide range of temperatures not readily combustible, does not melt or drip easy pigmentable with the LSR Colour Pastes Potential Applications Because of the outstanding properties Silopren LSR 2540 is particularly suitable for the following applications: textile coating for protective suits or conveyor belts, coating of glasfibre fabric sleeves, coating of fabrics for compensators, tents and other technical applications s.o.&&

Product Description
Supplier	Momentive
Generic	硅橡胶,LSR
Material Status	Commercial: Active
Features	Weather resistance is good,Low Viscosity,Low temperature toughness,Good stability,Ozone resistance,Heat Stabilized,Good coloring,HB
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.08	g/cm³	DIN 53479

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	40		DIN 53505

elastic body	Nominal value	Unit	Test method
tensile strength	6.50	MPa	DIN 53504
Tensile strain
fracture	500	%	DIN 53504
tear strength	25.0	kN/m	ASTM D624

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

THERMAL	Nominal value	Unit
Thermosetting components
Component A	按重量计算的混合比: 1.0
Component B	按重量计算的混合比: 1.0
Storage period
< 27℃	77	wk

Supplementary information	Nominal value	Unit	Test method
Vulcanization（175℃）	10.0	min

Uncured Properties	Nominal value	Unit	Test method
colour
—	Translucent
—	Translucent
viscosity			DIN 53018
20℃	100	Pa·s	DIN 53018
20℃	100	Pa·s	DIN 53018
storage stability
20 ℃	4300	min

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.