| About |
|---|
| SlLVER® PVC for Wire and Cable is produced based on high quality PVC resin by adding modified additives. The modified plastic entirely conforming to RoHS is of excellent mechanical and processing properties. In addition, the custom-made products should be developed by buyers‘ requirements in order to meet special usage.&& |
| Product Description | |
|---|---|
| Supplier | Silver Age |
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 to 1.45 | g/cm³ | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Low temperature bending | -20.0 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| insulation resistance | > 2.50 | Mohms·km |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | CM |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat resistant temperature | 60.0 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 88 to 92 | ||
| tensile strength | |||
| — | > 15.2 | MPa | |
| — | > 16.5 | MPa | |
| Tensile strain | |||
| fracture | > 180 | % | |
| fracture | > 170 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. after aging (100°C/168h) |
| 3. 4H |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |