| SIMONA® PP-Homopolymer white is a Polypropylene Homopolymer (PP Homopolymer) product. It is available in Europe, Latin America, or North America. Typical application: Food Contact Applications. Characteristics include: Food Contact Acceptable Homopolymer&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Homopolymer |
| Availabilitys | North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D792 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 43 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 98.9 | ℃ | |
| 1.8 MPa, unannealed | 57.2 | ℃ | |
| Crystallization peak temperature | |||
| DSC | 160 to 165 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 2.9E-4 | 1/℃ | ASTM D696 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| temperature range | 0 to 100 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| 1 second | 77 | ISO 868 | |
| Tensile modulus | 1520 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 34.5 | MPa | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. (10 °C/min) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |