| About |
|---|
| Sindustris ABS LAP274 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LAP274 are: Flame Rated Antistatic Typical application of Sindustris ABS LAP274: Electrical/Electronic Applications&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Antistatic property,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 30 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 490 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 90.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 87.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 94.0 | ℃ | ASTM D1525 5 |
| Relative temperature index | 60.0 | ℃ | UL 746 |
| Electrical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | ASTM D257 |
| Arc resistance | 5.00 | sec | ASTM D495 |
| Compared to the leakage tracing index | PLC 0 | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 98 | ASTM D785 | |
| Tensile modulus | |||
| 3.20 mm | 1660 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 3.20 mm | 43.1 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 3.20 mm | > 5.0 | % | ASTM D638 |
| Fracture, 3.20 mm | > 10 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2160 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 69.6 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Barrel rear temperature | 180 to 200 | °C | |
| Barrel middle temperature | 190 to 210 | °C | |
| Barrel front temperature | 200 to 220 | °C | |
| Nozzle temperature | 200 to 230 | °C | |
| Processing (melt) temperature | 210 to 240 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 3. 2.0 in/min |
| 4. 0.59 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 6. Solution A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |