| About |
|---|
| Sindustris ABS LTR667 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for extrusion, injection molding, or sheet extrusion. Important attributes of Sindustris ABS LTR667 are: Flame Rated Chemical Resistant Clarity Typical application of Sindustris ABS LTR667: Sheet&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Clarity,noise reduction,Solvent resistance,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 5.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 69 | J/m | ASTM D256 |
| -30℃，6.4mm | 69 | J/m | ASTM D256 |
| 23℃，3.2mm | 170 | J/m | ASTM D256 |
| 23℃，6.4mm | 150 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 94.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 86.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 92.0 | ℃ | ASTM D1525 5 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 90.0 | % | ASTM D1003 |
| Haze | 4.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 106 | ASTM D785 | |
| Pencil hardness | HB | ASTM D3363 | |
| Tensile modulus | |||
| 3.20 mm | 2060 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 3.20 mm | 43.1 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 3.20 mm | 8.0 | % | ASTM D638 |
| Fracture, 3.20 mm | 80 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2060 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 71.1 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Barrel rear temperature | 200 to 220 | °C | |
| Barrel middle temperature | 210 to 230 | °C | |
| Barrel front temperature | 220 to 240 | °C | |
| Nozzle temperature | 220 to 250 | °C | |
| Processing (melt) temperature | 220 to 250 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 3. 2.0 in/min |
| 4. 0.59 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |