| Sindustris PBT TE5007F is a Polycarbonate + PBT (PC+PBT) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PBT TE5007F are: Flame Rated Flame Retardant Typical application of Sindustris PBT TE5007F: Electrical/Electronic Applications&& |
| Product Description | |
|---|---|
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.60 to 1.0 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.20 mm | 58.8 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | > 100 | % | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 2300 | MPa | ASTM D790 |
| bending strength | |||
| 6.40 mm | 88.3 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 59 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 110 | ℃ | ASTM D648 |
| Melting peak temperature | 250 | ℃ | ASTM D3418 |
| Relative temperature index | 120 | ℃ | UL 746 |
| Electrical performance | 120 | ℃ | UL 746 |
| Impact mechanical performance | 120 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.50 mm | V-0 | ||
| 0.75 mm | V-0 | ||
| 1.00 mm | V-0 5VA | ||
| 1.60 mm | V-0 5VB |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 250 to 260 | °C | |
| Barrel middle temperature | 260 to 270 | °C | |
| Barrel front temperature | 260 to 270 | °C | |
| Nozzle temperature | 260 to 270 | °C | |
| Processing (melt) temperature | 260 to 270 | °C | |
| Mold temperature | 40.0 to 80.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.11 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |