| About |
|---|
| Sindustris PC GN1009RF is a Polycarbonate (PC) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PC GN1009RF are: Flame Rated Flame Retardant Halogen Free Impact Resistant Typical applications include: Housings Electrical/Electronic Applications&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High impact resistance,Halogen free,Flame Characteristics,V-2,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 18 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm | 60.8 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 100 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2450 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 96.1 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 780 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 103 | ℃ | ASTM D648 |
| Relative temperature index | 80.0 | ℃ | UL 746 |
| Electrical performance | 80.0 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.40 mm | V-2 | UL 94 | |
| 0.60 mm | V-0 | UL 94 | |
| 0.80 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85 to 95 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 245 to 260 | °C | |
| Barrel middle temperature | 260 to 275 | °C | |
| Barrel front temperature | 265 to 280 | °C | |
| Nozzle temperature | 270 to 285 | °C | |
| Processing (melt) temperature | 245 to 285 | °C | |
| Mold temperature | 70 to 90 | °C | |
| Back pressure | 0.200 to 0.600 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.39 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |