| About |
|---|
| B 4 Venezia is an extrusion grade developed for glossy applications.Easily extrudable even in large sheets, it has high gloss and high modulus. Designation: Thermoplastic ISO 2580-ABS 1,EGN,105-04-16-20 Applications It’s used in sectors that need high gloss and good processability.&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Excellent Processability,Good surface appearance,Low speed solidification point,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 6.0 | g/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 12 | kJ/m² | DIN 53453 |
| Charpy Unnotch Impact strength | DIN 53453 | ||
| -40℃ | 无断裂 | DIN 53453 | |
| 23℃ | 无断裂 | DIN 53453 | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 15 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 104 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 109 | ℃ | ISO 306/A120 |
| B120 | 104 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | ASTM D696 |
| Thermal conductivity coefficient | 0.17 | W/m/K | ASTM C177 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 kHz | 3.10 | IEC 60250 | |
| Dissipation factor | |||
| 1 kHz | 0.015 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Igniting temperature of the hot wire | |||
| 3 mm | 650 | ℃ | IEC 60695-2-13 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Designation | Thermoplastic ISO 2580-ABS 1,EGN,105-04-16-20 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 110 | ISO 2039-2 | |
| tensile strength | 50.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 45 | % | ASTM D638 |
| Bending modulus | 2150 | MPa | ASTM D790 |
| bending strength | 68.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Melt temperature | 190 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.079 in/min |
| 4. 4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |