| TECHNYL® POWDERS PA6 6300 HT 110 NATURAL (XP 1537/A) is a filled thermal stabilized Polyamide 6 natural powder engineered for the selective laser sintering technology (SLS). This product offers an excellent combination between thermal and mechanical properties. It presents mechanical properties at the level of injected PA6 parts. It enables the fabrication of durable and functional parts. Appropriate for prototyping, low and medium component serial production. Used in SLS for all sectors of industry, where a good mechanical and thermal resistance are required. Experimental name : XP 1537/A&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Heat Resistance, Good |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | 3D Printing, Laser Sintering/Melting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | |
| Apparent density | |||
| — | 0.60 | g/cm³ | |
| — | 0.80 | g/cm³ | |
| Particle size | |||
| D10 | 15.0 to 35.0 | µm | |
| D50 | 45.0 to 65.0 | µm | |
| D90 | 80.0 to 110 | µm | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 6300 | MPa | |
| tensile strength | |||
| Fracture, 23 ℃ | 77.0 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.9 | % | |
| Bending modulus | |||
| 23℃ | 6000 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 14 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 199 | ℃ | |
| 1.8 MPa, unannealed | 117 | ℃ | |
| Melting temperature | 210 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 3.8E+12 | ohms | |
| Volume resistivity | 2.1E+12 | ohms·cm | |
| Dielectric strength | 17 | kV/mm | |
| Dielectric constant | 2.70 | ||
| Dissipation factor | |||
| 1 Hz | 0.044 | ||
| Compared to the leakage tracing index | |||
| Solution A | < 599 | V |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Laser sintered parts |
| 3. bulk |
| 4. tapped |
| 5. after 7 cycles with 33% refresh rate |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |