| About |
|---|
| Sipchem EVA 2009 is a 9% ethylene – vinyl acetate copolymer resin, manufactured by IPC† in The Kingdom of Saudi Arabia using an Exxon-Mobil high-pressure tubular process. Film made from EVA 2009 exhibits superior impact strength and heat sealability. Applications: Meat Packaging, Meat Bags.&& |
| Product Description | |
|---|---|
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good heat sealing,High impact resistance,Copolymer |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.930 | g/cm³ | Internal Method |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| Vinyl acetate content | 9.0 | wt% | Internal Method |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| 1% secant, MD | 110 | MPa | |
| 1% secant, TD | 120 | MPa | |
| tensile strength | |||
| MD, fracture | 31.0 | MPa | |
| TD, fracture | 27.0 | MPa | |
| Tensile strain | |||
| MD, fracture | 330 | % | |
| TD, fracture | 660 | % | |
| Drop hammer impact | 250 | g | ASTM D1709-A |
| Elmandorf tear strength | |||
| MD | 120 | g | |
| TD | 100 | g |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 99.0 | ℃ | ASTM D3418 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |