| About |
|---|
| SKYGREEN® PN100 is a Polyethylene Terephthalate Glycol Comonomer (PETG) material. It is available in Asia Pacific, Europe, or North America for injection molding. Typical application of SKYGREEN® PN100 : Medical/Healthcare&& |
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | PETG |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.20 to 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.13 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.9 | kJ/m² | ISO 180 |
| 23℃ | 85 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 62.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 70.0 | ℃ | ASTM D648 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 90.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 26.0 | MPa | ASTM D638 |
| fracture | 26.0 | MPa | ISO 527-2/50 |
| yield | 50.0 | MPa | ASTM D638 |
| yield | 50.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 120 | % | ISO 527-2/50 |
| fracture | 120 | % | ASTM D638 |
| yield | 4.5 | % | ISO 527-2/50 |
| yield | 4.5 | % | ASTM D638 |
| Bending modulus | 2150 | MPa | ASTM D790 |
| Bending modulus | 2050 | MPa | ISO 178 |
| bending strength | 71.0 | MPa | ASTM D790 |
| bending strength | 69.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.050 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |