About |
---|
Product Description | |
---|---|
Supplier | SKC |
Generic | TPEE |
Material Status | Commercial: Active |
Features | High liquidity,Heat Stabilized |
Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.21 | g/cm³ | D792 |
Water absorption rate | |||
24 hrs | 0.6 | % | D570 |
Shrinkage rate | 1.5 | % | D955 |
Melt Flow Rate | |||
230℃,2.16Kg | 14 | g/10min | D1238 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
Shore hardness | |||
D-level | 63 | D2240 | |
tensile strength | |||
10% strain | 17 | MPa | D638 |
5% strain | 10 | MPa | D638 |
fracture | 43 | MPa | D638 |
Tensile strain | |||
fracture | 500 | % | D638 |
Bending modulus | |||
1.3mm/min | 314 | MPa | D790 |
tear strength | |||
51mm/mi | 180 | kN/m | D1004 |
Elastic strain | |||
Vertical rebound | 53 | % | D2632 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
melting point | 212 | ℃ | D3418 |
Hot deformation temperature | |||
0.45 MPa | 130 | ℃ | D648 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Cantilever notch impact strength | |||
23℃ | 无断裂 | D256 |
Process Conditions | |||
---|---|---|---|
Demoulding conditions | Nominal value | Unit | Test method |
Injection conditions | Nominal value | Unit | Test method |
Front barrel temperature | 225 | ℃ | |
Middle temperature | 220 | ℃ | |
Rear temperature | 210 | ℃ | |
Hard mold temperature | 225 | ℃ | |
Melt Temperature | 230 | ℃ | |
Front barrel temperature | 230 | ℃ | |
Middle temperature | 230 | ℃ | |
Rear temperature | 220 | ℃ | |
Nozzle temperature | 235 | ℃ | |
Mold temperature | 40 | ℃ |
Notes |
---|
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |