| About |
|---|
| SKYPET® HR is a Polyethylene Terephthalate (PET) material. It is available in Asia Pacific, Europe, or North America for injection blow molding, sheet extrusion, or thermoforming. Important attributes of SKYPET® HR are: Heat Resistant High Strength Wear Resistant Typical applications include: Bottles Containers Packaging Sheet&& |
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Durability,Heat Stabilized |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 to 0.60 | % | ASTM D955 |
| Color L（for crystalline pellets） | > 89 | % | |
| DEG Content | 1.2 | wt% | Internal Method |
| acid value | |||
| Carboxyl end group content | 33.00 | meq/kg | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -40℃ | 27 | J/m | |
| 23℃ | 38 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 69.0 | ℃ | ASTM D648 |
| Glass transition temperature | 80.0 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 88.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 | |
| tensile strength | |||
| yield | 50.0 | MPa | |
| fracture | 25.0 | MPa | |
| Tensile strain | |||
| yield | 4.5 | % | |
| fracture | > 50 | % | |
| Bending modulus | |||
| 1.27 mm | 2500 | MPa | ASTM D790 |
| bending strength | |||
| 1.27 mm | 83.0 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Scan rate 10 o C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |