About |
---|
Skyrol® SH52 is an optically clear and glossy polyester film. SH52 is pretreated on both sides with a coating to enhance toner adhesion. SH52 is used for PPC applications.&& |
Product Description | |
---|---|
Supplier | SKC |
Generic | PET |
Material Status | Commercial: Active |
Features | Good surface appearance,Optical performance,Good bond |
Availabilitys | North America,Asia Pacific,Europe |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.40 | g/cm³ | ASTM D1505 |
Shrinkage rate | Internal Method | ||
MD:150℃,0.0965 mm,30 min | 0.60 | % | Internal Method |
MD:150℃,0.125 mm,30 min | 0.50 | % | Internal Method |
TD:150℃,0.0965 mm,30 min | 0.60 | % | Internal Method |
TD:150℃,0.125 mm,30 min | 0.50 | % | Internal Method |
film | Nominal value | Unit | Test method |
---|---|---|---|
tensile strength | ASTM D882 | ||
MD, yield, 97 µ m | 207 | MPa | ASTM D882 |
MD, yield, 130 µ m | 186 | MPa | ASTM D882 |
TD, yield, 97 µ m | 228 | MPa | ASTM D882 |
TD, yield, 130 µ m | 200 | MPa | ASTM D882 |
Tensile strain | ASTM D882 | ||
MD, fracture, 97 µ m | 180 | % | ASTM D882 |
MD, fracture, 130 µ m | 190 | % | ASTM D882 |
TD, fracture, 97 µ m | 120 | % | ASTM D882 |
TD, fracture, 130 µ m | 120 | % | ASTM D882 |
optical performance | Nominal value | Unit | Test method |
---|---|---|---|
gloss | ASTM D523 | ||
96.5 µm | 142 | ASTM D523 | |
125 µm | 147 | ASTM D523 | |
Transmittance | ASTM D1003 | ||
96.5 µm | 92.0 | % | ASTM D1003 |
125 µm | 91.0 | % | ASTM D1003 |
Haze | ASTM D1003 | ||
96.5 µm | 3.2 | % | ASTM D1003 |
125 µm | 3.4 | % | ASTM D1003 |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
2. 96.5 µm |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |