| About |
|---|
| Skyrol® SH72S is an optically clear polyester film, slip treated on both sides, with high clarity,smooth surface, high gloss, and good dimensional stability.&& |
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good surface appearance,Smoothness,Good Dimensional Stability,Optical performance |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D1505 |
| Shrinkage rate | Internal Method | ||
| MD：150℃，0.05 mm，30 min | 1.2 | % | Internal Method |
| MD：150℃，0.1 mm，30 min | 1.2 | % | Internal Method |
| TD：150℃，0.05 mm，30 min | 0.50 | % | Internal Method |
| TD：150℃，0.1 mm，30 min | 0.50 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.40 | ASTM D1894 | |
| With oneself – dynamic | 0.30 | ASTM D1894 | |
| With oneself – static | 0.50 | ASTM D1894 | |
| With oneself – static | 0.40 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D882 | ||
| MD, yield, 50 µ m | 207 | MPa | ASTM D882 |
| MD, yield, 100 µ m | 179 | MPa | ASTM D882 |
| TD, yield, 50 µ m | 234 | MPa | ASTM D882 |
| TD, yield, 100 µ m | 207 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 50 µ m | 160 | % | ASTM D882 |
| MD, fracture, 100 µ m | 170 | % | ASTM D882 |
| TD, fracture, 50 µ m | 130 | % | ASTM D882 |
| TD, fracture, 100 µ m | 120 | % | ASTM D882 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D523 | ||
| 50 µm | 189 | ASTM D523 | |
| 100 µm | 188 | ASTM D523 | |
| Transmittance | ASTM D1003 | ||
| 50.0 µm | 90.0 | % | ASTM D1003 |
| 100 µm | 188.0 | % | ASTM D1003 |
| Haze | ASTM D1003 | ||
| 50 µm | 0.90 | % | ASTM D1003 |
| 100 µm | 1.1 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |