| About |
|---|
| Skyrol® SH92 is optically very clear, glossy, and has one side anti-static pretreated polyester film. SH91 is specially designed to improve ink / coating adhesion properties as well. With these advantages, SH92 is widely used as substrates for montage, overhead projection transparencies, color proofing and the like.&& |
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Optical performance,Good bond,Antistatic property |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D1505 |
| Shrinkage rate | Internal Method | ||
| MD：150℃，0.175 mm，30 min | 1.2 | % | Internal Method |
| TD：150℃，0.175 mm，30 min | 0.60 | % | Internal Method |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D882 | ||
| MD, yield, 180 µ m | 186 | MPa | ASTM D882 |
| TD, yield, 180 µ m | 186 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 180 µ m | 220 | % | ASTM D882 |
| TD, fracture, 180 µ m | 140 | % | ASTM D882 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 175 µm | 180 | ASTM D523 | |
| Transmittance | |||
| 175 µm | 90.0 | % | ASTM D1003 |
| Haze | |||
| 175 µm | 2.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 175 µm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |