SLOVALEN® PH 59 GF 30

About
Modified homopolymer PP for injection moulding, chemically reinforced with 30% glass fibre, with high strength, rigidity and toughness, adapted thermal properties, decreased shrinkage. Suitable for automotive, engineering, electrical and consumer goods industry. With the increasing content of GF also the toughness, tensile and bending strength, modulus in tension and bending increase and the shrinkage decreases as well as the heat application increases up to 150°C. Additional drying of the material is not necessary. Delivered in natural mode and in the full RAL colour scale. Production of the fuel tank caps for the transport vehicles, shells for the textile industry.&&

About

Modified homopolymer PP for injection moulding, chemically reinforced with 30% glass fibre, with high strength, rigidity and toughness, adapted thermal properties, decreased shrinkage. Suitable for automotive, engineering, electrical and consumer goods industry. With the increasing content of GF also the toughness, tensile and bending strength, modulus in tension and bending increase and the shrinkage decreases as well as the heat application increases up to 150°C. Additional drying of the material is not necessary. Delivered in natural mode and in the full RAL colour scale. Production of the fuel tank caps for the transport vehicles, shells for the textile industry.&&

Product Description
Generic	PP not specified
Material Status	Commercial: Active
Features	Good Rigidity,Chemical coupling,Ultra high toughness,Homopolymer,HB
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.13	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	6.0	g/10min	ISO 1133
Shrinkage rate			STM 64 0808
TD	0.82	%	STM 64 0808
MD	0.72	%	STM 64 0808

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	5650	MPa	ISO 527-2
tensile strength
yield	80.0	MPa	ISO 527-2
Tensile strain
yield	30	%	ISO 527-2
Bending modulus	4890	MPa	ISO 178
bending strength	128	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-20℃	9.0	kJ/m²	ISO 179
23℃	11	kJ/m²	ISO 179
Charpy Unnotch Impact strength			ISO 179
-20℃	45	kJ/m²	ISO 179
23℃	50	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	134	℃	ISO 75-2/B
Vicat Softening Temp	162	℃	ISO 306/B
Melting temperature
DSC	160	℃	ISO 3146

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	2.0	hr
Processing (melt) temperature	200 to 250	°C
Mold temperature	40 to 80	°C
Injection pressure	70.0 to 120	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.