| Modified homopolymer PP for injection moulding, chemically reinforced with 30% glass fibre, contains the modifier of mechanical properties. Thermo stable. Increased strength in comparison with unfilled PP. Applied in all industry branches. Increased strength, toughness, modulus in tension due to the modification. Delivered in natural mode and in the full RAL colour scale.&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Chemical coupling,Heat Stabilized,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.0 | g/10min | ISO 1133 |
| Shrinkage rate | STM 64 0808 | ||
| TD | 1.2 | % | STM 64 0808 |
| MD | 0.78 | % | STM 64 0808 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6400 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 77.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 3.0 | % | ISO 527-2 |
| Bending modulus | 5100 | MPa | ISO 178 |
| bending strength | 117 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20℃ | 6.0 | kJ/m² | ISO 179 |
| 23℃ | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -20℃ | 41 | kJ/m² | ISO 179 |
| 23℃ | 43 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 160 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 163 | ℃ | ISO 306/B |
| Melting temperature | |||
| DSC | 160 | ℃ | ISO 3146 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 250 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Injection pressure | 70.0 to 120 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |