SLOVAMID® 6 GF 25

About
PA 6 for injection moulding, chemically strengthened with 25% of glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-goods industry. Application: grips of electrotools, hobby tools, gears, covers of electric appliances, cooling skrews of blowers, electromotors, carrying parts in the automotive industry. With the increasing content of GF also the toughness, bending and tensile strength increase as well as the heat application increases up to 250°C and the shrinkage decreases. GF 60 achieves modulus 18000 MPa – of the aluminium alloy values. Delivered in natural mode and in the full RAL colour scale.&&

About

PA 6 for injection moulding, chemically strengthened with 25% of glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-goods industry. Application: grips of electrotools, hobby tools, gears, covers of electric appliances, cooling skrews of blowers, electromotors, carrying parts in the automotive industry. With the increasing content of GF also the toughness, bending and tensile strength increase as well as the heat application increases up to 250°C and the shrinkage decreases. GF 60 achieves modulus 18000 MPa – of the aluminium alloy values. Delivered in natural mode and in the full RAL colour scale.&&

Product Description
Generic	PA6
Material Status	Commercial: Active
Features	Good Rigidity,Chemical coupling,Ultra high toughness,HB
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.30	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	3.0	g/10min	ISO 1133
Shrinkage rate			STM 64 0808
TD	1.4	%	STM 64 0808
MD	0.50	%	STM 64 0808
water content	0.15	%	ISO 960

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	7400	MPa	ISO 527-2
tensile strength
yield	140	MPa	ISO 527-2
Tensile strain
yield	3.0	%	ISO 527-2
Bending modulus	6300	MPa	ISO 178
bending strength	200	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-20℃	7.0	kJ/m²	ISO 179
23℃	10	kJ/m²	ISO 179
Charpy Unnotch Impact strength			ISO 179
-20℃	27	kJ/m²	ISO 179
23℃	50	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	200	℃	ISO 75-2/B
Vicat Softening Temp	210	℃	ISO 306/B
Melting temperature
DSC	220	℃	ISO 3146

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94
Igniting temperature of the hot wire	650	℃	IEC 60695-2-13

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	4.0	hr
Processing (melt) temperature	250 to 280	°C
Mold temperature	70 to 90	°C
Injection pressure	70.0 to 120	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.