SLOVAMID® 6 GF 35 TS

About
PA 6 for injection moulding, chemically reinforced with 35% glass fibre, heat stabilized, mouldings resistant against long-time heat impact up to 170°C. Used in environment, where long-time temperatures up to 200°C occur. Decrease in tensile strength by 50% after 5000 hours at 170°C. Application: grips of electrotools, hobby tools, gears, covers of electric appliances. Heat stabilization predetermines these prodcts to an environment with longtime heat stress like eg.: intake piping, cylinder heads, induction coils, carrying parts in the motor fixing in the motor area. Delivered in black colour.&&

About

PA 6 for injection moulding, chemically reinforced with 35% glass fibre, heat stabilized, mouldings resistant against long-time heat impact up to 170°C. Used in environment, where long-time temperatures up to 200°C occur. Decrease in tensile strength by 50% after 5000 hours at 170°C. Application: grips of electrotools, hobby tools, gears, covers of electric appliances. Heat stabilization predetermines these prodcts to an environment with longtime heat stress like eg.: intake piping, cylinder heads, induction coils, carrying parts in the motor fixing in the motor area. Delivered in black colour.&&

Product Description
Generic	PA6
Material Status	Commercial: Active
Features	Chemical coupling,Heat Stabilized,HB
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.38	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	3.0	g/10min	ISO 1133
Shrinkage rate			STM 64 0808
TD	0.80	%	STM 64 0808
MD	0.60	%	STM 64 0808
water content	0.15	%	ISO 960

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	10500	MPa	ISO 527-2
tensile strength
yield	190	MPa	ISO 527-2
Tensile strain
yield	2.5	%	ISO 527-2
Bending modulus	6850	MPa	ISO 178
bending strength	200	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-20℃	13	kJ/m²	ISO 179
23℃	15	kJ/m²	ISO 179
Charpy Unnotch Impact strength			ISO 179
-20℃	95	kJ/m²	ISO 179
23℃	100	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	215	℃	ISO 75-2/B
Vicat Softening Temp	200	℃	ISO 306/B
Melting temperature
DSC	222	℃	ISO 3146

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	8.0E+13	ohms	IEC 60093
Volume resistivity	5.0E+13	ohms·cm	IEC 60093
Dielectric strength	20	kV/mm	IEC 60243-1
Compared to the leakage tracing index	475	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94
Igniting temperature of the hot wire	650	℃	IEC 60695-2-13

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	4.0	hr
Processing (melt) temperature	250 to 270	°C
Mold temperature	70 to 90	°C
Injection pressure	70.0 to 120	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.