| About |
|---|
| PA 6 for injection moulding, chemically strengthened with 50% of glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-goods industry. Application: grips of electrotools, hobby tools, gears, covers of electric appliances, cooling skrews of blowers, electromotors, carrying parts in the automotive industry. Very good surface finish of products and very good processability. Delivered in natural mode and in the full RAL colour scale.PA 6 for injection moulding, lightly impacted&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,Good surface appearance,Heat Stabilized,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.55 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 10 | g/10min | ISO 1133 |
| Shrinkage rate | STM 64 0808 | ||
| TD | 0.60 | % | |
| MD | 0.50 | % | |
| water content | 0.15 | % | ISO 960 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 14500 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 210 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 2.0 | % | ISO 527-2 |
| Bending modulus | 12500 | MPa | ISO 178 |
| bending strength | 290 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20℃ | 11 | kJ/m² | |
| 23℃ | 13 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -20℃ | 80 | kJ/m² | |
| 23℃ | 85 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 212 | ℃ | ISO 306/B |
| Melting temperature | |||
| DSC | 222 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 8.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 5.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 40 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 575 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 | |
| Igniting temperature of the hot wire | 650 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90.0 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 260 to 280 | °C | |
| Mold temperature | 90.0 to 100 | °C | |
| Injection pressure | 90.0 to 150 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |