| About |
|---|
| PA 66 for injection moulding, chemically reinforced with 20 % glass beads, light stabilized, suitable for high strength and high impacted mouldings. Used in automotive, engineering and electrical industry. Can be used in environment, in which longtime heat impact of up to 200°C occurs. Decrease in tensile strength by 50 % after 5000 hours at 170°C. The heat stabilization predetermines the products to environment with longtime heat exposure.&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Chemical coupling,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 275℃，0.325kg | 3.0 | g/10min | ISO 1133 |
| Shrinkage rate | STM 64 0808 | ||
| TD | 1.7 | % | STM 64 0808 |
| MD | 1.6 | % | STM 64 0808 |
| water content | 0.15 | % | ISO 960 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3100 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 45.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 20 | % | ISO 527-2 |
| Bending modulus | 2500 | MPa | ISO 178 |
| bending strength | 65.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20℃ | 1.0 | kJ/m² | ISO 179 |
| 23℃ | 2.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -20℃ | 40 | kJ/m² | ISO 179 |
| 23℃ | 40 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 250 | ℃ | ISO 306/B |
| Melting temperature | |||
| DSC | 260 | ℃ | ISO 3146 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 | |
| Igniting temperature of the hot wire | 650 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Injection pressure | 70.0 to 120 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |