SLOVAMID® 66 GF 20/1M

About
Chemically reinforced with 20 % glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. With the increasing content of FG also the toughness, tensile and bending strength increase, the shrinkage decreases and the heat application increases up to 250°C. Application: hobby tools, covers of electrotools, electromotors, cooling screws of blowers, gear wheels, carrying parts in the automotive industry like eg. brake cables. Delivered in natural mode and in the full RAL colour scale.&&

About

Chemically reinforced with 20 % glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. With the increasing content of FG also the toughness, tensile and bending strength increase, the shrinkage decreases and the heat application increases up to 250°C. Application: hobby tools, covers of electrotools, electromotors, cooling screws of blowers, gear wheels, carrying parts in the automotive industry like eg. brake cables. Delivered in natural mode and in the full RAL colour scale.&&

Product Description
Generic	PA66
Material Status	Commercial: Active
Features	Flame Characteristics,High Heat Resistance,HB
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Melt Flow Rate
275℃，0.325kg	5.0	g/10min	ISO 1133
Shrinkage rate			STM 64 0808
TD	1.1	%	STM 64 0808
MD	0.80	%	STM 64 0808
water content	0.15	%	ISO 960

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	7700	MPa	ISO 527-2
tensile strength
yield	135	MPa	ISO 527-2
Tensile strain
yield	3.0	%	ISO 527-2
Bending modulus	5200	MPa	ISO 178
bending strength	180	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-20℃	5.0	kJ/m²	ISO 179
23℃	5.5	kJ/m²	ISO 179
Charpy Unnotch Impact strength			ISO 179
-20℃	37	kJ/m²	ISO 179
23℃	40	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	250	℃	ISO 75-2/B
Vicat Softening Temp	250	℃	ISO 306/B

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94
Igniting temperature of the hot wire	650	℃	IEC 60695-2-13

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	4.0	hr
Processing (melt) temperature	250 to 280	°C
Mold temperature	50 to 90	°C
Injection pressure	80.0 to 120	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.