Smart™ 121S - SOLIAO

About
Smart™ 121S, metallocene LLDPE, is an ethylene-octene copolymer produced via Nexlene™ technology. Smart™ 121S performs well in a wide range of various food & non-food packaging films with excellent sealing property, impact strength, and processibility. Typical Performance: Excellent low seal initiation temperature and hot tack strength Superior impact strength and transparency Outstanding bubble stability & processability Compiles with: US. FDA 21 CFR 177.1520 EU. No 10/2011 Additives: Antiblock: 2000 ppm Slip: 1000 ppm&&

About

Smart™ 121S, metallocene LLDPE, is an ethylene-octene copolymer produced via Nexlene™ technology. Smart™ 121S performs well in a wide range of various food & non-food packaging films with excellent sealing property, impact strength, and processibility. Typical Performance: Excellent low seal initiation temperature and hot tack strength Superior impact strength and transparency Outstanding bubble stability & processability Compiles with: US. FDA 21 CFR 177.1520 EU. No 10/2011 Additives: Antiblock: 2000 ppm Slip: 1000 ppm&&

Product Description
Supplier	SKC
Generic	mLLDPE
Material Status	Commercial: Active
Features	Excellent Processability,Good Clarity,High impact resistance,Smoothness,High anti-blocking,Food contact compliance,Low density,Octene copolymer,Copolymer,Low temperature heat sealing
Availabilitys	North America,Asia Pacific,Europe
Process Methods	Film extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.913	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	1.0	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	40	µm	ASTM D374
Secant modulus
1% secant, MD: 40 µ m	118	MPa
1% secant, TD: 40 µ m	130	MPa
tensile strength
MD, fracture, 40 µ m	49.0	MPa
TD, fracture, 40 µ m	50.0	MPa
Tensile strain
MD, fracture, 40 µ m	580	%
TD, fracture, 40 µ m	650	%
Drop hammer impact
40 µm	> 1000	g	ASTM D1709-A
Elmandorf tear strength
MD：40 µm	11	g
TD：40 µm	23	g

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	101	℃	ASTM D1525
Melting temperature	111	℃	Internal Method

optical performance	Nominal value	Unit	Test method
Haze	10	%	ASTM D1003

Supplementary information	Nominal value	Unit	Test method
Sealing Initial Temperature	101	℃	Internal Method

Process Conditions
Squeeze description	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method

Melt temperature	160 to 180	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.