| About |
|---|
| Smoothblend® PC-1201 is a wear resistance polycarbonate compound offering superb lubricity by incorporating PTFE and carbon fiber. It is developed for applications demanding stringent wear resistant and low friction performance.&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Lubricating,Good wear resistance,Solvent resistance,Heat Stabilized,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 to 0.40 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 120 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.5 | % | ASTM D638 |
| Bending modulus | 10500 | MPa | ASTM D790 |
| bending strength | 160 | MPa | ASTM D790 |
| friction coefficient | ASTM D1894 | ||
| Steel – Dynamic | 0.28 | ASTM D1894 | |
| Steel – Static | 0.13 | ASTM D1894 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 4.0 mm | 140 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 275 to 280 | °C | |
| Barrel middle temperature | 280 to 285 | °C | |
| Barrel front temperature | 285 to 290 | °C | |
| Nozzle temperature | 290 to 295 | °C | |
| Processing (melt) temperature | 275 to 300 | °C | |
| Mold temperature | 85 to 110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |