| About |
|---|
| SoarnoL™ DC3203F is one of the standard grades of SoarnoL™, its ethylene content is 32 mol% with a low MFR (melt flow rate). SoarnoL™ DC3203F has excellent barrier to gases, and is primarily used in co-extrusion blow-molded containers, co-extruded film and tube applications.&& |
| Product Description | |
|---|---|
| Generic | EVOH |
| Material Status | Commercial: Active |
| Features | Low liquidity,Low odor,Food contact compliance,Copolymer |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 210℃，2.16kg | 3.2 | g/10min | |
| Ethylene composition | 32.0 | wt% | Internal Method |
| Volatiles | < 0.30 | % | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen permeability | |||
| 20℃，20 µm | 0.500 | cm³/m²/24 hr | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 61.0 | ℃ | DSC |
| Melting temperature | 183 | ℃ | DSC |
| Crystallization peak temperature | |||
| DSC | 160 | ℃ | DSC |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 180 | °C | |
| Barrel 2 zone temperature | 200 | °C | |
| Barrel 3 zone temperature | 220 | °C | |
| Barrel 4 zone temperature | 230 | °C | |
| Barrel 5 zone temperature | 230 | °C | |
| Connector temperature | 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Measured with Micromeritics Gas Pycnometer |
| 3. Measured with OXTRAN 2/20 (MOCON), 65%RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |