| About |
|---|
| SoarnoL™ H4815B is a 48 mol% ethylene content grade of SoarnoL™ with a high melt flow rate. SoarnoL™ H4815B has the best water resistance of al SoarnoL™ grades and good gas barrier property, especially in high humidity environments. Its gas barrier property is not drastically lower at high humidity. This resin is used in co-extruded film, co-extrusion coating and shrink packaging.&& |
| Product Description | |
|---|---|
| Generic | EVOH |
| Material Status | Commercial: Active |
| Features | Low odor,Food contact compliance,Moisture resistance,Copolymer |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 210℃，2.16kg | 15 | g/10min | |
| Ethylene composition | 48.0 | wt% | Internal Method |
| Volatiles | < 0.30 | % | |
| Density | 1.12 | g/cm³ | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen permeability | |||
| 20℃，20 µm | 2.30 | cm³/m²/24 hr | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 48.0 | ℃ | DSC |
| Melting temperature | 158 | ℃ | DSC |
| Crystallization peak temperature | |||
| DSC | 138 | ℃ | DSC |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 170 to 190 | °C | |
| Barrel 2 zone temperature | 185 to 210 | °C | |
| Barrel 3 zone temperature | 200 to 230 | °C | |
| Barrel 4 zone temperature | 200 to 230 | °C | |
| Barrel 5 zone temperature | 200 to 230 | °C | |
| Connector temperature | 200 to 230 | °C | |
| Screw length to diameter ratio | 28.0:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Measured with Micromeritics Gas Pycnometer |
| 3. Measured with OXTRAN 2/20 (MOCON), 65%RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |