| About |
|---|
| Sofprene P® 40D 11I HFM 150 is a Thermoplastic Polyolefin Elastomer (TPO (POE)) material. It is available in Europe, Latin America, or North America for injection molding. Primary attribute of Sofprene P® 40D 11I HFM 150: REACH Compliant. Typical application of Sofprene P® 40D 11I HFM 150: Sporting Goods&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 25 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 100% strain | 7.30 | MPa | ASTM D638 |
| yield | 12.5 | MPa | |
| — | 18.5 | MPa | |
| Tensile strain | |||
| fracture | 850 | % | ASTM D412 |
| tear strength | 76.0 | kN/m | ASTM D624 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 3 seconds | 40 | ASTM D2240 | |
| Bending modulus | 150 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 170 | °C | |
| Barrel middle temperature | 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 7.9 in/min |
| 3. Die C, 7.9 in/min |
| 4. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |