| About |
|---|
| Solanyl® C1203 is an end compound suitable for injection & compression molding applications. Solanyl® C1203 can be processed on conventional lines. Solanyl® C1203 is acompetitive alternative for currently used biodegradable plastics & polyolefins for a wide range of applications. Solanyl® C1203 has a natural feel & look. Solanyl® C1203 is biodegradable with a biobased and plant based content of > 28%.&& |
| Product Description | |
|---|---|
| Generic | 生物可降解聚合物 |
| Material Status | Commercial: Active |
| Features | Renewable resources,Biodegradable |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Charpy Notched Impact Strength | |||
| injection molding | 10 to 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| injection molding | > 10 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| Injection molding | 11 to 21 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| Injection molding | 无断裂 | ISO 180/1U | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | < 55.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | < 55.0 | ℃ | ISO 75-2/A |
| Glass transition temperature | 50.0 to 55.0 | ℃ | DSC |
| Vicat Softening Temp | 49.0 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 110 to 130 | ℃ | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Water Activity | 0.200 to 0.400 | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, injection molding | 35 | ISO 868 | |
| Tensile modulus | |||
| injection molding | < 200 | MPa | |
| Cutting, injection molding | 60.0 to 150 | MPa | |
| tensile strength | |||
| injection molding | 9.00 to 11.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, injection molding | 10 | % | |
| Fracture, injection molding | > 200 | % | |
| Bending modulus | |||
| injection molding | 200 to 400 | MPa | ISO 178 |
| bending strength | |||
| injection molding | 2.00 to 7.00 | MPa | ISO 178 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.25 to 1.30 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 to 0.80 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 170℃，2.16kg | 2.0 to 5.0 | g/10min | Internal Method |
| 190℃，5.0kg | 19 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 8.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | < 0.0 | % | ISO 294-4 |
| water content | 1.5 to 2.5 | % | Internal Method |
| Apparent viscosity of melt | |||
| 140℃，10.0 sec^-1 | 3050 | Pa·s | |
| 140℃，100 sec^-1 | 850 | Pa·s | |
| 140℃，1000 sec^-1 | 210 | Pa·s | |
| 170℃，10.0 sec^-1 | 2340 | Pa·s | |
| 170℃，100 sec^-1 | 810 | Pa·s | |
| 170℃，1000 sec^-1 | 200 | Pa·s |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |