| Solanyl® C1401 is an end compound suitable for injection molding applications and is specially developed to obtain a biopolymer with properties like hard PS. Solanyl® C1401 can be processed on conventional injection molding machines. Solanyl® C1401 is biodegradable and has a biobased or plant derived material content of >76%.&& |
| Product Description | |
|---|---|
| Generic | 生物可降解聚合物 |
| Material Status | Commercial: Active |
| Features | Renewable resources,Biodegradable,Food contact compliance,Compostable |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ISO 1183/A |
| Apparent density | 0.70 to 0.80 | g/cm³ | ISO 60 |
| Melt Flow Rate | 10 to 25 | g/10min | ISO 1133 |
| Shrinkage rate | < 0.10 | % | ISO 294-4 |
| water content | 2.5 to 4.0 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| injection molding | 1.0 to 2.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| injection molding | 10 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 50.0 | ℃ | ISO 75-2/B |
| Glass transition temperature | 50.0 to 55.0 | ℃ | DSC |
| Vicat Softening Temp | 55.0 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 140 to 155 | ℃ | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Water Activity | > 0.300 | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, injection molding | > 80 | ISO 868 | |
| Tensile modulus | |||
| injection molding | 2900 | MPa | ISO 527-2 |
| tensile strength | |||
| injection molding | 31.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, injection molding | 1.0 to 2.0 | % | ISO 527-2 |
| Bending modulus | |||
| injection molding | 2700 | MPa | ISO 178 |
| bending strength | |||
| injection molding | 51.0 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |