| About |
|---|
| Solanyl® C2001 is an end compound suitable for glossy extrusion applications with PP or PS like properties. Solanyl® C2001can be processed on conventional extrusion lines suitable for (multi-layer) products. Solanyl®C2001 is a competitive alternative for currently used biodegradable plastics for a wide range of applications. Solanyl® C2001has a natural feel and look. Solanyl® C2001 is biodegradable and has a biobased or plant derived material content of > 50%. Applications are: Consumer goods & Packaging & Agriculture products Thermoform applications (e.g.cups, boxes & trays) Plates and sheets Groundwork applications like pipes Extruded profiles&& |
| Product Description | |
|---|---|
| Generic | 生物可降解聚合物 |
| Material Status | Commercial: Active |
| Features | Renewable resources,Biodegradable,Food contact compliance,Compostable |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| film | Nominal value | Unit | Test method |
| film thickness | |||
| test | 100 to 1000 | µm | |
| tensile strength | |||
| MD, yield | 21.0 to 23.0 | MPa | |
| TD, yield | 18.0 to 21.0 | MPa | |
| MD | 23.0 to 28.0 | MPa | |
| TD | 20.0 to 26.0 | MPa | |
| Tensile strain | |||
| MD, yield | 5.0 to 15 | % | |
| TD, yield | 5.0 to 15 | % | |
| MD, fracture | > 150 | % | |
| TD, fracture | > 90 | % | |
| Dart impact equipped with measuring instruments | > 5.00 | J | ISO 7765-2 |
| Elmandorf tear strength | |||
| MD | > 15 | N | |
| TD | > 10 | N | |
| Oxygen transfer rate | |||
| 23℃，50% RH，100 µm | 300 to 500 | cm³/m²/24 hr | ISO 15105-2 |
| Water vapor transmittance | |||
| 23℃，75% RH | 40 to 90 | g/m²/24 hr | |
| 23℃，85% RH | 120 to 150 | g/m²/24 hr | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| injection molding | 39 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 55.0 | ℃ | ISO 75-2/B |
| Glass transition temperature | 50.0 to 55.0 | ℃ | DSC |
| Vicat Softening Temp | 56.0 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 145 to 160 | ℃ | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Water Activity | < 0.250 | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, injection molding | 60 | ISO 868 | |
| Tensile modulus | |||
| injection molding | 1000 to 1200 | MPa | |
| Cutting, injection molding | > 900 | MPa |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.25 to 1.30 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 to 0.80 | g/cm³ | ISO 60 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 17.0 to 18.0 | cm³/10min | |
| 190℃，2.16 kg | 9.00 to 10.0 | cm³/10min | |
| Shrinkage rate | < 2.0 | % | ISO 294-4 |
| water content | < 0.30 | Internal Method | |
| Ash Content | 1.0 to 2.0 | % | Internal Method |
| Apparent viscosity of melt | |||
| 190℃，10.0 sec^-1 | 872 | Pa·s | |
| 190℃，10.0 sec^-1 | 598 | Pa·s | |
| 190℃，100 sec^-1 | 551 | Pa·s | |
| 190℃，100 sec^-1 | 462 | Pa·s | |
| 190℃，1000 sec^-1 | 196 | Pa·s | |
| 190℃，1000 sec^-1 | 172 | Pa·s |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.03%w |
| 3. 0.9%w |
| 4. 25-35 µm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |