Solanyl® C2201

About
Solanyl® C2201 is an end compound suitable for extrusion. Solanyl® C2201 can be processed on conventional extrusion lines. Solanyl® C2201 is a competitive alternative for currently used biodegradable plastics, hard PP & PS for a wide range of applications. Solanyl® C2201 can be mixed with most biopolyesters or starch based plastics to reduce costs. Solanyl® C2201 has a natural feel and look. Solanyl® C2201 is biodegradable and has a biobased or plant based content of > 67%. Applications in which Solanyl® C2201 can be used are: Consumer goods & Packaging Agriculture products Thermoform applications Cups, boxes & trays Plates and sheets Groundwork applications like pipes Extruded profiles&&

Product Description
Generic生物可降解聚合物
Material StatusCommercial: Active
FeaturesRenewable resources,Biodegradable,Food contact compliance,Compostable
AvailabilitysAfrica & Middle East ,North America,Latin America,Asia Pacific,Europe
Process MethodsExtrusion

Technical Data
filmNominal valueUnitTest method
film thickness
test400 to 1000µm
tensile strength
injection molding30.0 to 32.0MPaISO 527-2
MD, yield26.0 to 34.0MPa
TD, yield20.0 to 23.0MPa
MD24.0 to 30.0MPa
TD18.0 to 22.0MPa
Oxygen transfer rate
23℃,50% RH400 to 600cm³/m²/24 hrISO 15105-2
Water vapor transmittance
38℃,90% RH200 to 300g/m²/24 hrISO 15106-1

IMPACTNominal valueUnitTest method
Charpy Notched Impact Strength
injection molding2.0 to 3.0kJ/m²ISO 179/1eA
Charpy Unnotch Impact strength
injection molding20 to 70kJ/m²ISO 179/1eU
Impact strength of cantilever beam notch
Injection molding2.0 to 3.0kJ/m²ISO 180-1A
Notched impact strength of cantilever beam
Injection molding20 to 60kJ/m²ISO 180/1U

THERMALNominal valueUnitTest method
Hot deformation temperature
0.45 MPa, unannealed55.0ISO 75-2/B
1.8 MPa, unannealed50.0ISO 75-2/A
Glass transition temperature57.0DSC
Vicat Softening Temp55.0 to 60.0ISO 306/A
Melting temperature
DSC140 to 160Internal Method

FLAME CHARACTERISTICSNominal valueUnitTest method
Burning rate68mm/min

Supplementary informationNominal valueUnitTest method
Water Activity0.150 to 0.250 Internal Method

MECHANICALNominal valueUnitTest method
Shore hardness
Shaw’s D, injection molding75 to 80 ISO 868
Tensile modulus
injection molding1700 to 2000MPa
Cutting, injection molding800 to 1400MPa
Tensile strain
Yield, injection molding5.0%
Fracture, injection molding10 to 30%
Bending modulus
injection molding1800MPaISO 178
bending strength
injection molding47.0 to 52.0MPaISO 178

PHYSICALNominal valueUnitTest method
Density1.25 to 1.30g/cm³ISO 1183
Apparent density0.70 to 0.80g/cm³ISO 60
Melt Flow Rate
170℃,2.16kg2.0 to 6.0g/10min
190℃,5.0kg> 10g/10minISO 1133
Melt Volume Rate
190℃,2.16 kg5.00 to 7.00cm³/10minISO 1133
Spiral flow length47.0cm
Shrinkage rate< 1.0%ISO 294-4
water content< 1.1 Internal Method
Ash Content2.0 to 2.5%Internal Method
Apparent viscosity of melt
160℃,10.0 sec^-19600Pa·s
160℃,100 sec^-12900Pa·s
160℃,1000 sec^-1600Pa·s
170℃,10.0 sec^-1977Pa·s
170℃,100 sec^-1336Pa·s
170℃,1000 sec^-1141Pa·s

Notes
1. Typical properties: these are not to be construed as specifications.
2. Mold Temperature: 77°F
3. 40-400 µm
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.