| About |
|---|
| Solanyl ® C2204 is an end compound suitable for extrusion. Solanyl ® C2204 can be processed on conventional extrusion lines. Solanyl ® C2204 is a competitive alternative for currently used biodegradable plastics, like LDPE and PPcopol for a wide range of applications. Solanyl ® C2204 is in particular suitable for (multi-layer) (semi-)flexible products. Solanyl ® C2204 can be mixed with most biopolyesters or starch based plastics to reduce costs. Solanyl ® C2204 has a natural feel and look. Solanyl ® C2204 is biodegradable with a biobased or plant based content of >60%. Applications are: Consumer goods & Packaging &Agriculture products Thermoform applications: Cups, boxes & trays Plates and sheets (incl. multi-layers) Extruded flexible profiles&& |
| Product Description | |
|---|---|
| Generic | 生物可降解聚合物 |
| Material Status | Commercial: Active |
| Features | Renewable resources,Biodegradable,Food contact compliance,Compostable |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Bending modulus | |||
| injection molding | 900 | MPa | ISO 178 |
| bending strength | |||
| injection molding | 24.0 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 400 to 5000 | µm | |
| Tensile modulus | |||
| MD | > 0.700 | MPa | |
| TD | > 0.500 | MPa | |
| tensile strength | |||
| injection molding | 21.0 | MPa | ISO 527-2 |
| MD, yield | 23.0 to 26.0 | MPa | |
| TD, yield | 13.0 to 18.0 | MPa | |
| MD | 23.0 to 28.0 | MPa | |
| TD | 13.0 to 19.0 | MPa | |
| Tensile strain | |||
| MD, yield | 3.0 to 5.0 | % | |
| TD, yield | 8.0 to 12 | % | |
| MD, fracture | 100 to 200 | % | |
| TD, fracture | 40 to 120 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| injection molding | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| injection molding | > 100 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 55.0 | ℃ | DSC |
| Vicat Softening Temp | 60.0 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 150 to 165 | ℃ | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Water Activity | < 0.400 | Internal Method |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 to 0.80 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 10 to 15 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 190℃，5 kg | > 20.0 | cm³/10min | ISO 1133 |
| Spiral flow length | 25.0 to 30.0 | cm | |
| Shrinkage rate | < 4.0 | % | ISO 294-4 |
| water content | 0.50 to 1.2 | Internal Method | |
| Ash Content | < 2.0 | % | Internal Method |
| Apparent viscosity of melt | |||
| 170℃，10.0 sec^-1 | 3290 | Pa·s | |
| 170℃，100 sec^-1 | 1070 | Pa·s | |
| 170℃，1000 sec^-1 | 360 | Pa·s | |
| 180℃，10.0 sec^-1 | 1570 | Pa·s | |
| 180℃，100 sec^-1 | 860 | Pa·s | |
| 180℃，1000 sec^-1 | 232 | Pa·s |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mold Temperature: 77°F |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |