| About |
|---|
| Solef® 1006 PVDF is a very low viscosity homopolymer resin mainly used in injection molding or in multifilament extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PVDF |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Homopolymer,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 30 to 40 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 23℃，24hr | < 0.040 | % | ASTM D570 |
| Shrinkage rate | |||
| Linear | 2.0 to 3.0 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 1 second, 2.00 mm | 73 to 80 | ASTM D2240 | |
| Tensile modulus | |||
| 23℃，2 mm | 1800 to 2600 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 23 ℃, 2 mm | 30.0 to 50.0 | MPa | ASTM D638 |
| Yield, 23 ℃, 2 mm | 50.0 to 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 2 mm | 20 to 300 | % | ASTM D638 |
| Yield, 23 ℃, 2 mm | 5.0 to 10 | % | ASTM D638 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-10 wheels | 5.00 to 10.0 | mg | ASTM D4060 |
| friction coefficient | ASTM D1894 | ||
| dynamic | 0.15 to 0.35 | ASTM D1894 | |
| static state | 0.20 to 0.40 | ASTM D1894 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃，4mm，2m/s | 25.0 to 75.0 | J/m | ASTM D6110 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -40.0 | ℃ | ASTM D4065 |
| Vicat Softening Temp | 135 to 145 | ℃ | ASTM D1525 5 |
| Melting temperature | 170 to 175 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 134 to 144 | ℃ | ASTM D3418 |
| Linear coefficient of thermal expansion | |||
| MD：0~40℃ | 1.4E-4 | 1/℃ | ASTM D696 |
| specific heat | ASTM E968 | ||
| 23℃ | 1200 | J/kg/℃ | ASTM E968 |
| 100℃ | 1600 | J/kg/℃ | ASTM E968 |
| Thermal conductivity coefficient | |||
| 23℃ | 0.20 | W/m/K | ASTM C177 |
| Crystallization heat | 54.0 to 60.0 | J/g | ASTM D3417 |
| Crystallization point | 137 to 144 | ℃ | ASTM D3418 |
| Fusion heat | 58.0 to 67.0 | J/g | ASTM D3417 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 23℃ | 20 to 25 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 23 ℃，1.0 mm，1 kHz | 7.00 to 10.0 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.10 mm | V-0 | UL 94 | |
| Oxygen Index（3.00 mm） | 44 | % | ASTM D2863 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |