| About |
|---|
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PVDF |
| Material Status | Commercial: Active |
| Features | Ultra High Viscosity,Homopolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.78 | g/cm³ | ISO 1183 |
| Shrinkage rate | 2-3 | % | |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8 | g/10min | ASTM D1238 |
| 230℃，5.0kg | 24 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 23℃ | <=0.040 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 2.00 mm | 60 | ASTM D2240 | |
| Tensile modulus | |||
| 23℃，2 mm | 2100 to 2300 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 23 ℃, 50 mm/min | 35.0-50.0 | MPa | ASTM D638 |
| Yield, 23 ℃, 50 mm/min | 15-18 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 2 mm | 600-750 | % | ASTM D638 |
| Yield, 23 ℃, 2 mm | 12-15 | % | ASTM D638 |
| Elastic modulus | 36-48 | MPa | ASTM D638 |
| Bending modulus | 36-41 | MPa | ASTM D790 |
| friction coefficient | 0.2-0.3 | ASTM D1894 | |
| friction coefficient | |||
| static state | 0.2-0.4 | ASTM D1894 | |
| Taber wear and tear | |||
| Mg/1000 times | 5.0-15 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | |||
| TG | -29 | ℃ | DMTA |
| melting point | 135 | 10℃/min | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 92 | ℃ | ASTM D3418 |
| heat of fusion | |||
| Completely melted at 80 ℃ | 23.0 | J/g | |
| Crystallization heat | 24 | J/g | |
| Linear coefficient of thermal expansion | |||
| 20℃ | 150-180 | 1/℃ | ASTM D696 |
| Specific heat capacity | |||
| 23℃ | 1.2 | J/g | |
| 100℃ | 1.6 | J/g | |
| Thermal conductivity | 0.180 | W/m/K | ASTM C177 |
| Hot deformation temperature | |||
| 0.46 MPa，150℃，16 hrs | 62 | ℃ | ASTM D648 |
| 1.8 MPa，150℃，16 hrs | 40 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| 10N，4mm | 120 | ℃ | ISO 306 |
| Embrittlement temperature | -22.0 | ℃ | ASTM D746A |
| decomposition temperature | |||
| Reduce weight by 1% in the air | 340-375 | °C |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，4mm | 18 | kJ/m² | ASTM D256 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |