| About |
|---|
| Solef® 5130 PVDF is an ultra high viscosity grade that gives the best adhesion ideal for its usage in lithium batteries.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PVDF |
| Material Status | Commercial: Active |
| Features | Ultra High Viscosity,Good bond |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.75 to 1.78 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | < 0.20 | % | ASTM D543 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 1000 to 1500 | MPa | ASTM D638 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -40.0 | ℃ | DSC |
| Melting temperature | 160 to 168 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 135 to 140 | ℃ | ASTM D3418 |
| Heat of Fusion | 40.0 to 48.0 | J/g | ASTM D3418 |
| thermal stability | > 375 | ℃ | TGA |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 30g |
| 3. 0.039 in/min |
| 4. 80°C to end of melting |
| 5. @ 1% weight loss |
| 6. Voltage < 1V, after 2 min - 500 V @ 23°C |
| 7. Intensity = 10 mA, after 2 min @ 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |