| About |
|---|
| Solef FPCH08/0001 is a low-viscosity PVDF resin typically processed by extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PVDF |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 5.5 to 11 | g/10min | |
| 230℃，5.0kg | 16 to 30 | g/10min | |
| Water absorption rate | |||
| 23℃，24hr | < 0.040 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃，2 mm | 1800 to 2500 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃, 2 mm | 50.0 to 60.0 | MPa | |
| Fracture, 23 ℃, 2 mm | 30.0 to 50.0 | MPa | |
| Tensile strain | |||
| Yield, 23 ℃, 2 mm | 5.0 to 10 | % | |
| Fracture, 23 ℃, 2 mm | 20 to 300 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 170 to 175 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 134 to 144 | ℃ | ASTM D3418 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 23 ℃，1 mm | 20 to 25 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 23 ℃，1 kHz | 7.00 to 10.0 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.20 mm | V-0 | UL 94 | |
| Extreme oxygen index | |||
| 3.0 mm | 44 | % | ASTM D2863 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type IV, 0.039 in/min |
| 3. Type IV, 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |