| About |
|---|
| Solumer™ 8613L is an ethylene-octene copolymer produced via Nexlene™ technology. Solumer™ 8613L has excellent flow characteristics that provides ease in processing and is highly effective as an impact modifier or as a component in injection. |
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| Melt Flow Rate | 0.863 | g/cm³ | ASTM D792 |
| 190℃，2.16kg | 13 | g/10min | ASTM D1238 |
| Mooney viscosity | |||
| ML 1+4，121℃ | 3 | MU | ASTM D1646 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 26 | KN/m | ASTM D624 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -57 | ℃ | Internal Method |
| Melting temperature | 42 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 1 second | 63 | ASTM D2240 | |
| Shore D, 1 second | 14 | ASTM D2240 | |
| Tensile modulus | |||
| 100% | 1.77 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 2.35 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | >1000 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 7.55 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |