| About |
|---|
| Somos® PerFORM produces strong, stiff, high-temperature resistant composite parts on standard 355 nm stereolithography machines. This material’s lower viscosity makes processing parts faster. It exhibits superior sidewall quality, along with excellent detail resolution compared to other composite stereolithography materials. Applications Somos® PerFORM is an easy to process material with excellent detail resolution. It is the ideal material for creating strong, stiff parts with excellent high heat resistance, including wind tunnel models for aerospace and automotive applications, as well as rapid tooling for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | 3D打印材料 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,High Heat Resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.61 | g/cm³ | |
| Water absorption rate | ASTM D570 | ||
| balance | 0.20 | % | ASTM D570 |
| balance | 0.10 | % | ASTM D570 |
| viscosity | |||
| 30℃ | 1.00 | Pa·s | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| — | 17 | J/m | ASTM D256 |
| — | 20 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed | 119 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 82.0 | ℃ | ASTM D648 |
| Glass transition temperature | ASTM E1545 | ||
| — | 72.0 | ℃ | ASTM E1545 |
| — | 81.0 | ℃ | ASTM E1545 |
| Linear coefficient of thermal expansion | |||
| MD | ASTM E831 | ||
| -40 to 0 ℃ | 2.6E-5 | cm/cm/℃ | ASTM E831 |
| -40 to 0 ℃ | 3.0E-5 | cm/cm/℃ | ASTM E831 |
| 0 to 50 ℃ | 3.4E-5 | cm/cm/℃ | ASTM E831 |
| 0 to 50 ℃ | 4.9E-5 | cm/cm/℃ | ASTM E831 |
| 50 to 100 ℃ | 6.0E-5 | cm/cm/℃ | ASTM E831 |
| 50 to 100 ℃ | 7.9E-5 | cm/cm/℃ | ASTM E831 |
| 100 to 150 ℃ | 8.1E-5 | cm/cm/℃ | ASTM E831 |
| 100 to 150 ℃ | 9.5E-5 | cm/cm/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | ASTM D149 | ||
| — | 26 | kV/mm | ASTM D149 |
| — | 25 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 60 Hz | 4.00 | ASTM D150 | |
| 1 kHz | 3.90 | ASTM D150 | |
| 1 kHz | 3.80 | ASTM D150 | |
| 1 MHz | 3.60 | ASTM D150 | |
| 1 MHz | 3.70 | ASTM D150 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Critical Exposure | 7.80 | mJ/cm² | |
| Penetration depth | 109.2 | µm |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s D | 94 | ASTM D2240 | |
| Shaw’s D | 93 | ASTM D2240 | |
| Tensile modulus | ASTM D638 | ||
| — | 10500 | MPa | ASTM D638 |
| — | 9800 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| — | 68.0 | MPa | ASTM D638 |
| — | 80.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| fracture | 1.1 | % | ASTM D638 |
| fracture | 1.2 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| — | 10000 | MPa | ASTM D790 |
| — | 9030 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| — | 120 | MPa | ASTM D790 |
| — | 146 | MPa | ASTM D790 |
| Poisson’s ratio | ASTM D638 | ||
| — | 0.32 | ASTM D638 | |
| — | 0.33 | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. UV Postcure & Thermal Postcure |
| 3. UV Postcure |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |