| About |
|---|
| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | PBT/PC |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Medium Viscosity,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 6.0 | g/10min | ASTM D1238 |
| Shrinkage rate | 0.5~1.0 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.08 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 540 | J/m | ASTM D256 |
| -30℃，6.4mm | – | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear expansion coefficient | 13 | × 10-5cm/cm·℃ | ASTM D696 |
| Vicat Softening Temp | 162 | ℃ | ASTM D1525 |
| melting point | 224 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 1.8 MPa | 100 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 3.20 mm，50 mm/min | 44 | MPa | ASTM D638 |
| Tensile strain | |||
| 3.20 mm，50 mm/min | 100< | % | ASTM D638 |
| Bending modulus | |||
| 5 mm/min，3.20 mm | 1,764 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm，5 mm/min | 69 | MPa | ASTM D790 |
| Rockwell hardness | |||
| M-level | 80 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 100~120 | ℃ | |
| Drying time | 3~5 | hr | |
| Control moisture content | ≤ 0.04 | % | |
| Mold temperature | 30~70 | ℃ | |
| Nozzle temperature | 245~255 | ℃ | |
| Front temperature of material barrel | 245~260 | ℃ | |
| Temperature in the middle of the barrel | 235~250 | ℃ | |
| Temperature at the rear of the barrel | 220~240 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |