| Product Description | |
|---|---|
| Supplier | SUQING |
| Material Status | Commercial: Negative |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| crystallization | 1.3 | g/cm³ | ISO 1183 |
| Amorphous | 1.26 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 0.07 | % | ISO 62-1 | |
| 0.4 | % | ISO 62-1 | |
| Shrinkage rate | |||
| MD | 1.3 | % | ISO 294-4 |
| TD | 1 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| 23℃ | 85 | D 级 | ISO 868 |
| tensile strength | |||
| Yield, 23 ℃ | 100 | MPa | ISO 527 |
| Tensile strain | |||
| Fracture, 23 ℃ | 40 | % | ISO 527 |
| bending strength | |||
| Yield, 23 ℃ | 170 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 4200 | MPa | ISO 178 |
| compressive strength | |||
| 23℃ | 125 | MPa | ISO 604 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 6 | kJ/m² | ISO 179/1eA | |
| Impact strength of cantilever beam notch | |||
| 6.5 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 343 | ℃ | ISO 11357 |
| Hot deformation temperature | |||
| 1.8 Mpa | 152 | ℃ | ISO 75-f |
| Glass transition temperature | |||
| origin | 143 | ℃ | ISO 11357 |
| Specific heat capacity | |||
| 23℃ | 2.2 | kJ/kg/℃ | DSC |
| Linear coefficient of thermal expansion | |||
| Below Tg along the flow direction | 45 | ppm/K | ISO 11359 |
| Above Tg along the flow direction | 120 | ppm/K | ISO 11359 |
| ISO 22007-4 | |||
| 23℃ | 0.29 | W/m/K | ISO 22007-4 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23 ℃，1V | 10^16 | ohms·cm | IEC 60093 |
| 275 ℃ | 10^9 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 2 mm | 23 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 150 | V | IEC 60112 |
| Dielectric constant | |||
| 23 ℃, 1 kHz | 3.2 | IEC 60250 | |
| 23 ℃, 50 Hz | 4.5 | IEC 60250 | |
| Loss tangent | |||
| 23℃, 1MHz | 0.003 | IEC 60250 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| viscosity | |||
| 400℃ | 330 | Pa·s | ISO 11443 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |