| About |
|---|
| This product is a 70% special mineral reinforced modified polyphenylene sulfide with a stable coefficient of thermal expansion. Especially suitable for pursuing ultra-high dimensional stability and ultra-high precision in environments such as light, heat, and electricity, it can be widely used in communication, military, semiconductor, and other fields. |
| Product Description | |
|---|---|
| Supplier | SUQING |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.84 | g/cm³ | ISO 1183 |
| Water Absorption | |||
| 23℃，24 h | 0.01 | % | ISO 62 |
| Viscosity | |||
| 310℃，1000/s | 250 | Pa·s | IS0 11443 |
| Melt Flow Rate | 29.3 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | 68.8 | MPa | ISO 527-2 |
| Tensile Strain | |||
| brk | 0.6 | % | ISO 527 |
| Flexural Strength | 103 | MPa | ISO 178 |
| Flexural Modulus | 13060 | MPa | ISO 178 |
| Tensile Modulus | 11723 | MPa | ISO 527 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy notched Impact strength | 1.5 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| HDT | |||
| 1.8 MPa | 185 | ℃ | ISO 75-1/-2 |
| Coeff.of linear therm expansion | |||
| flow | 2 | ×10-5/℃ | |
| vertical | 2 | ×10-5/℃ |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| insulation Strength | 14 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Rear Temperature -Zone 1 | 300 to 340 | °C | |
| Middle Temperature -Zone 2 | 300 to 340 | °C | |
| Front Temperature -Zone 3 | 300 to 340 | °C | |
| Mold Temperature | 120 to 150 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |