| About |
|---|
| 30% Glass Reinforced, High Flow, Flame Retardant, Halogen free and free of red phosphorous&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | High liquidity,Halogen free,Flame Characteristics,Low to no phosphorus content |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.53 | g/cm³ | |
| Shrinkage rate | |||
| TD | 1.0 | % | |
| MD | 0.40 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.8 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12500 | MPa | |
| tensile strength | |||
| fracture | 140 | MPa | |
| Tensile strain | |||
| fracture | 1.7 | % | |
| Bending modulus | 12500 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 9.0 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 290 | ℃ | |
| 1.8 MPa, unannealed | 290 | ℃ | |
| Melting temperature | 295 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 3.5E-5 | 1/℃ | |
| TD | 4.5E-5 | 1/℃ | |
| Relative temperature index | |||
| Electrical performance, 0.75 mm | 65.0 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | |
| Dielectric strength | 33 | kV/mm | |
| Relative permittivity | |||
| 1 MHz | 4.10 | ||
| 1.00 GHz | 3.90 | ||
| Compared to the leakage tracing index | 425 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.75 mm | V-0 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. (10°C/min) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |